Roman Travertine classico cross cut, Roman Travertine classico cross cut Tivoli Rome Italy

Roman Travertine Classico Cross Cut

Classic Travertine Cross Cut, also known as Classic Roman Travertine , belongs to the categories of the beige travertines. The material has a cloudy pattern. Classic Travertine Cross cut is an essentially beige travertine with very light clouds ranging from Light to dark Beige, sometimes with shades of silver. The structure shows its compactness and homogeneity. Generally there are no significant pores or cavities.  Extracted directly from the travertine quarries in Tivoli, Rome, Italy, the availability of blocks, slabs and cut to sizes is good. Classic roman travertine cross cut.  is easily and often used for floors, cladding and kitchens tops. The finishes can be honed, polished, tumbled or saw cut.

Contact us - Phone  +39 0774 355737 -This email address is being protected from spambots. You need JavaScript enabled to view it.

Physical - Mechanical Characteristic ( ASTM STANDARD)

  • Apparent Specific Weight - C97 - 2517Kg/m³
  • Absorption Coefficient - C97 - 058%
  • Compressive Strenght Dry - C170 - 73,22 Mpa/Mpa
  • Compressive Strenght Wet - C170 - 68,39 Mpa/Mpa
  • Modulus of Rupture Dry - C99 - 10,71 Mpa/Mpa
  • Modulus of Rupture Wet - C99 - 11,67 Mpa/Mpa
  • Flexural Strenght Dry - C880 - 10,21 Mpa/Mpa
  • Flexural Strenght Wet - C880 - 11,60 Mpa/Mpa
  • Resistance to Abrasion - C241 - 14,65 Mpa/Mpa
  • Static Coefficient Of Friction Dry - C1028 - 0,60 Mpa/Mpa
  • Static Coefficient Of Friction Wet - C1028 - 0,57Mpa/Mpa

Chemical Composition:

  • Apparent and Insoluble Silicons in Hydrochloric Acid - 0,012
  • Soluble Silicon Acid, Calculeted as Qnhhydride - 0,636
  • CO2 - 43,495
  • SO3 - 0,230
  • P2O5 - 0,017
  • A12O3 - 0,170
  • Fe2O3 - 0,031
  • FeO - 0,016
  • CaO - 54,712
  • MgO - 0,541
  • Other Indeterminates and Losses 0,140
  • Specific Weight 2,457